EN 1.3521 Steel vs. ACI-ASTM CB7Cu-1 Steel

Both EN 1.3521 steel and ACI-ASTM CB7Cu-1 steel are iron alloys. They have 77% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3521 steel and the bottom bar is ACI-ASTM CB7Cu-1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
300 to 420
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 490 to 1390
960 to 1350

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1500
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.6
Embodied Energy, MJ/kg 19
38
Embodied Water, L/kg 52
130

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 49
34 to 48
Strength to Weight: Bending, points 18 to 35
28 to 35
Thermal Diffusivity, mm2/s 12
4.6
Thermal Shock Resistance, points 14 to 41
32 to 45

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.14 to 0.19
0 to 0.070
Chromium (Cr), % 0.8 to 1.1
15.5 to 17.7
Copper (Cu), % 0 to 0.3
2.5 to 3.2
Iron (Fe), % 96.8 to 98.2
72.3 to 78.4
Manganese (Mn), % 1.0 to 1.3
0 to 0.7
Nickel (Ni), % 0
3.6 to 4.6
Niobium (Nb), % 0
0 to 0.35
Nitrogen (N), % 0
0 to 0.050
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030