EN 1.3523 Steel vs. ACI-ASTM CF16F Steel

Both EN 1.3523 steel and ACI-ASTM CF16F steel are iron alloys. They have 69% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3523 steel and the bottom bar is ACI-ASTM CF16F steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 220
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 520 to 1460
530

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
980
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 19
47
Embodied Water, L/kg 53
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 52
19
Strength to Weight: Bending, points 18 to 36
19
Thermal Diffusivity, mm2/s 12
4.3
Thermal Shock Resistance, points 15 to 42
12

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.17 to 0.22
0 to 0.16
Chromium (Cr), % 1.0 to 1.3
18 to 21
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.5 to 97.9
61.3 to 72.8
Manganese (Mn), % 1.1 to 1.4
0 to 1.5
Molybdenum (Mo), % 0
0 to 1.5
Nickel (Ni), % 0
9.0 to 12
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.17
Selenium (Se), % 0
0.2 to 0.35
Silicon (Si), % 0 to 0.4
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040