MakeItFrom.com
Menu (ESC)

EN 1.3537 Steel vs. AWS ENiCrCoMo-1

EN 1.3537 steel belongs to the iron alloys classification, while AWS ENiCrCoMo-1 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3537 steel and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 620 to 730
710

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
75
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.5
11
Embodied Energy, MJ/kg 21
140
Embodied Water, L/kg 54
340

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 22 to 26
23
Strength to Weight: Bending, points 21 to 23
21
Thermal Shock Resistance, points 18 to 22
19

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.93 to 1.1
0.050 to 0.15
Chromium (Cr), % 1.7 to 2.0
21 to 26
Cobalt (Co), % 0
9.0 to 15
Copper (Cu), % 0 to 0.3
0 to 0.5
Iron (Fe), % 96.4 to 97.8
0 to 5.0
Manganese (Mn), % 0.25 to 0.45
0.3 to 2.5
Molybdenum (Mo), % 0.15 to 0.3
8.0 to 10
Nickel (Ni), % 0
38.6 to 61.7
Niobium (Nb), % 0
0 to 1.0
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.15 to 0.45
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.015
Residuals, % 0
0 to 0.5