EN 1.3537 Steel vs. EN 1.3536 Steel
Both EN 1.3537 steel and EN 1.3536 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.3537 steel and the bottom bar is EN 1.3536 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 220 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 730 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 440 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 43 | |
| 41 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 2.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.6 |
| Embodied Energy, MJ/kg | 21 | |
| 21 |
| Embodied Water, L/kg | 54 | |
| 55 |
Common Calculations
| PREN (Pitting Resistance) | 2.6 | |
| 2.8 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 23 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 22 |
| Thermal Diffusivity, mm2/s | 12 | |
| 11 |
| Thermal Shock Resistance, points | 18 to 22 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.050 |
| Carbon (C), % | 0.93 to 1.1 | |
| 0.93 to 1.1 |
| Chromium (Cr), % | 1.7 to 2.0 | |
| 1.7 to 2.0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.3 |
| Iron (Fe), % | 96.4 to 97.8 | |
| 96 to 97.4 |
| Manganese (Mn), % | 0.25 to 0.45 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0.2 to 0.35 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.45 | |
| 0.15 to 0.45 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |