EN 1.3541 Stainless Steel vs. ASTM A372 Grade H Steel

Both EN 1.3541 stainless steel and ASTM A372 grade H steel are iron alloys. They have 87% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3541 stainless steel and the bottom bar is ASTM A372 grade H steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
200 to 280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 710
650 to 910

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 770
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
45
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.3
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.5
Embodied Energy, MJ/kg 27
20
Embodied Water, L/kg 100
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
23 to 32
Strength to Weight: Bending, points 23
21 to 27
Thermal Diffusivity, mm2/s 8.1
12
Thermal Shock Resistance, points 26
19 to 27

Alloy Composition

Carbon (C), % 0.43 to 0.5
0.3 to 0.4
Chromium (Cr), % 12.5 to 14.5
0.4 to 0.65
Iron (Fe), % 83.4 to 87.5
97.3 to 98.3
Manganese (Mn), % 0 to 1.0
0.75 to 1.1
Molybdenum (Mo), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010