EN 1.3541 Stainless Steel vs. ASTM Grade HH Steel

Both EN 1.3541 stainless steel and ASTM grade HH steel are iron alloys. They have 74% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.3541 stainless steel and the bottom bar is ASTM grade HH steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 710
580

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Corrosion, °C 390
440
Maximum Temperature: Mechanical, °C 770
1100
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
14
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
20
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 1.9
3.7
Embodied Energy, MJ/kg 27
53
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 14
27
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
21
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 8.1
3.8
Thermal Shock Resistance, points 26
12

Alloy Composition

Carbon (C), % 0.43 to 0.5
0.2 to 0.5
Chromium (Cr), % 12.5 to 14.5
24 to 28
Iron (Fe), % 83.4 to 87.5
52.9 to 64.8
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
11 to 14
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040