Both EN 1.3549 stainless steel and AWS ER110S-1 are iron alloys. They have 81% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is AWS ER110S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 730
870

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
47
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 10
4.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.8
Embodied Energy, MJ/kg 37
25
Embodied Water, L/kg 130
55

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
31
Strength to Weight: Bending, points 24
26
Thermal Diffusivity, mm2/s 5.6
13
Thermal Shock Resistance, points 26
26

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.85 to 1.0
0 to 0.090
Chromium (Cr), % 17 to 19
0 to 0.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 77.5 to 82
92.8 to 96.3
Manganese (Mn), % 0 to 1.0
1.4 to 1.8
Molybdenum (Mo), % 0.9 to 1.3
0.25 to 0.55
Nickel (Ni), % 0
1.9 to 2.6
Phosphorus (P), % 0 to 0.040
0 to 0.010
Silicon (Si), % 0 to 1.0
0.2 to 0.55
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0.070 to 0.12
0 to 0.040
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.5