EN 1.3549 Stainless Steel vs. AWS ERNiCrFe-6
EN 1.3549 stainless steel belongs to the iron alloys classification, while AWS ERNiCrFe-6 belongs to the nickel alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is AWS ERNiCrFe-6.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1370 |
| Melting Onset (Solidus), °C | 1390 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 21 | |
| 13 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 55 |
| Density, g/cm3 | 7.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 9.8 |
| Embodied Energy, MJ/kg | 37 | |
| 140 |
| Embodied Water, L/kg | 130 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 27 | |
| 21 |
| Strength to Weight: Bending, points | 24 | |
| 19 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 3.3 |
| Thermal Shock Resistance, points | 26 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 17 to 19 | |
| 14 to 17 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 77.5 to 82 | |
| 0 to 8.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 2.0 to 2.7 |
| Molybdenum (Mo), % | 0.9 to 1.3 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 67 to 81.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 2.5 to 3.5 |
| Vanadium (V), % | 0.070 to 0.12 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |