EN 1.3549 Stainless Steel vs. SAE-AISI 1070 Steel

Both EN 1.3549 stainless steel and SAE-AISI 1070 steel are iron alloys. They have 81% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is SAE-AISI 1070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 730
640 to 760

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 910
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
50
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
12

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
19
Embodied Water, L/kg 130
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
23 to 27
Strength to Weight: Bending, points 24
21 to 24
Thermal Diffusivity, mm2/s 5.6
14
Thermal Shock Resistance, points 26
21 to 25

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.65 to 0.75
Chromium (Cr), % 17 to 19
0
Iron (Fe), % 77.5 to 82
98.3 to 98.8
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0.9 to 1.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Vanadium (V), % 0.070 to 0.12
0