EN 1.3549 Stainless Steel vs. SAE-AISI 5015 Steel

Both EN 1.3549 stainless steel and SAE-AISI 5015 steel are iron alloys. They have 81% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is SAE-AISI 5015 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 730
430

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 910
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
52
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
19
Embodied Water, L/kg 130
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
15
Strength to Weight: Bending, points 24
16
Thermal Diffusivity, mm2/s 5.6
14
Thermal Shock Resistance, points 26
13

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.12 to 0.17
Chromium (Cr), % 17 to 19
0.3 to 0.5
Iron (Fe), % 77.5 to 82
98.4 to 99.13
Manganese (Mn), % 0 to 1.0
0.3 to 0.5
Molybdenum (Mo), % 0.9 to 1.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040
Vanadium (V), % 0.070 to 0.12
0