EN 1.3549 Stainless Steel vs. N08221 Nickel
EN 1.3549 stainless steel belongs to the iron alloys classification, while N08221 nickel belongs to the nickel alloys. They have 48% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is N08221 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 980 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1440 |
| Melting Onset (Solidus), °C | 1390 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 44 |
| Density, g/cm3 | 7.7 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 7.9 |
| Embodied Energy, MJ/kg | 37 | |
| 110 |
| Embodied Water, L/kg | 130 | |
| 240 |
Common Calculations
| PREN (Pitting Resistance) | 22 | |
| 40 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 27 | |
| 21 |
| Strength to Weight: Bending, points | 24 | |
| 19 |
| Thermal Shock Resistance, points | 26 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0.85 to 1.0 | |
| 0 to 0.025 |
| Chromium (Cr), % | 17 to 19 | |
| 20 to 22 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 77.5 to 82 | |
| 22 to 33.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.9 to 1.3 | |
| 5.0 to 6.5 |
| Nickel (Ni), % | 0 | |
| 39 to 46 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.0 |
| Vanadium (V), % | 0.070 to 0.12 | |
| 0 |