EN 1.3549 Stainless Steel vs. N08926 Stainless Steel

Both EN 1.3549 stainless steel and N08926 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 730
740

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 400
420
Maximum Temperature: Mechanical, °C 910
1100
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 21
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.6
6.2
Embodied Energy, MJ/kg 37
84
Embodied Water, L/kg 130
200

Common Calculations

PREN (Pitting Resistance) 22
45
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 24
22
Thermal Diffusivity, mm2/s 5.6
3.2
Thermal Shock Resistance, points 26
16

Alloy Composition

Carbon (C), % 0.85 to 1.0
0 to 0.020
Chromium (Cr), % 17 to 19
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 77.5 to 82
41.7 to 50.4
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.3
6.0 to 7.0
Nickel (Ni), % 0
24 to 26
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0.070 to 0.12
0