EN 1.3553 Steel vs. Grade Ti-Pd16 Titanium
EN 1.3553 steel belongs to the iron alloys classification, while grade Ti-Pd16 titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.3553 steel and the bottom bar is grade Ti-Pd16 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 720 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 320 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1660 |
| Melting Onset (Solidus), °C | 1570 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 540 |
| Thermal Conductivity, W/m-K | 24 | |
| 22 |
| Thermal Expansion, µm/m-K | 12 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 36 |
| Embodied Energy, MJ/kg | 130 | |
| 600 |
| Embodied Water, L/kg | 96 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 35 |
| Strength to Weight: Axial, points | 24 | |
| 24 |
| Strength to Weight: Bending, points | 21 | |
| 26 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 8.9 |
| Thermal Shock Resistance, points | 21 | |
| 30 |
Alloy Composition
| Carbon (C), % | 0.78 to 0.86 | |
| 0 to 0.1 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 80.7 to 83.7 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 4.7 to 5.2 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.96 |
| Tungsten (W), % | 6.0 to 6.7 | |
| 0 |
| Vanadium (V), % | 1.7 to 2.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |