EN 1.3555 Steel vs. EN AC-51200 Aluminum
EN 1.3555 steel belongs to the iron alloys classification, while EN AC-51200 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.3555 steel and the bottom bar is EN AC-51200 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 67 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 75 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 170 |
| Melting Completion (Liquidus), °C | 1500 | |
| 640 |
| Melting Onset (Solidus), °C | 1450 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 910 |
| Thermal Expansion, µm/m-K | 13 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.3 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 74 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 7.9 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 9.6 |
| Embodied Energy, MJ/kg | 81 | |
| 150 |
| Embodied Water, L/kg | 90 | |
| 1150 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 51 |
| Strength to Weight: Axial, points | 27 | |
| 24 |
| Strength to Weight: Bending, points | 23 | |
| 31 |
| Thermal Shock Resistance, points | 22 | |
| 10 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 84.5 to 92 |
| Carbon (C), % | 0.1 to 0.15 | |
| 0 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.1 |
| Iron (Fe), % | 85.4 to 87.7 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0 | |
| 8.0 to 10.5 |
| Manganese (Mn), % | 0.15 to 0.35 | |
| 0 to 0.55 |
| Molybdenum (Mo), % | 4.0 to 4.5 | |
| 0 |
| Nickel (Ni), % | 3.2 to 3.6 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0.1 to 0.25 | |
| 0 to 2.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Tungsten (W), % | 0 to 0.15 | |
| 0 |
| Vanadium (V), % | 1.0 to 1.3 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |