EN 1.3555 Steel vs. SAE-AISI H19 Steel
Both EN 1.3555 steel and SAE-AISI H19 steel are iron alloys. They have 90% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.3555 steel and the bottom bar is SAE-AISI H19 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 720 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 260 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1540 |
| Melting Onset (Solidus), °C | 1450 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 460 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 22 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 7.5 |
| Embodied Energy, MJ/kg | 81 | |
| 110 |
| Embodied Water, L/kg | 90 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 18 | |
| 13 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 27 | |
| 24 to 68 |
| Strength to Weight: Bending, points | 23 | |
| 22 to 43 |
| Thermal Shock Resistance, points | 22 | |
| 21 to 59 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.15 | |
| 0.32 to 0.45 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 4.0 to 4.8 |
| Cobalt (Co), % | 0 | |
| 4.0 to 4.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.25 |
| Iron (Fe), % | 85.4 to 87.7 | |
| 81.4 to 85.5 |
| Manganese (Mn), % | 0.15 to 0.35 | |
| 0.2 to 0.5 |
| Molybdenum (Mo), % | 4.0 to 4.5 | |
| 0.3 to 0.55 |
| Nickel (Ni), % | 3.2 to 3.6 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.1 to 0.25 | |
| 0.2 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 to 0.15 | |
| 3.8 to 4.5 |
| Vanadium (V), % | 1.0 to 1.3 | |
| 1.8 to 2.2 |