EN 1.3563 Steel vs. Commercially Pure Zirconium
EN 1.3563 steel belongs to the iron alloys classification, while commercially pure zirconium belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is EN 1.3563 steel and the bottom bar is commercially pure zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 1850 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 43 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.7 |
| Embodied Water, L/kg | 52 | |
| 450 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 65 | |
| 18 |
| Strength to Weight: Bending, points | 22 to 43 | |
| 19 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 20 to 54 | |
| 56 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0.4 to 0.46 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 96.8 to 98.4 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 94.7 to 100 |