EN 1.3567 Steel vs. SAE-AISI 1080 Steel
Both EN 1.3567 steel and SAE-AISI 1080 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.3567 steel and the bottom bar is SAE-AISI 1080 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 220 | |
| 220 to 260 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1420 | |
| 770 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 9.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.5 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 | |
| 19 |
| Embodied Water, L/kg | 52 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 50 | |
| 27 to 31 |
| Strength to Weight: Bending, points | 18 to 36 | |
| 24 to 26 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 15 to 42 | |
| 25 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0.17 to 0.23 | |
| 0.75 to 0.88 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 96.8 to 98.4 | |
| 98.1 to 98.7 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |