EN 1.3576 Steel vs. EN 1.4835 Stainless Steel

Both EN 1.3576 steel and EN 1.4835 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3576 steel and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 220
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 490 to 1420
750

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
1150
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.7
3.3
Embodied Energy, MJ/kg 22
47
Embodied Water, L/kg 53
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 50
27
Strength to Weight: Bending, points 17 to 36
24
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 14 to 42
16

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.17 to 0.23
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 0.35 to 0.65
20 to 22
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 95.5 to 97.5
62 to 68.4
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.6 to 2.0
10 to 12
Nitrogen (N), % 0
0.12 to 0.2
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
1.4 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015