EN 1.3956 Stainless Steel vs. AWS ERTi-7

EN 1.3956 stainless steel belongs to the iron alloys classification, while AWS ERTi-7 belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3956 stainless steel and the bottom bar is AWS ERTi-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 27
20
Fatigue Strength, MPa 240
190
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 79
40
Tensile Strength: Ultimate (UTS), MPa 650
340
Tensile Strength: Yield (Proof), MPa 330
280

Thermal Properties

Latent Heat of Fusion, J/g 300
420
Maximum Temperature: Mechanical, °C 1080
320
Melting Completion (Liquidus), °C 1420
1670
Melting Onset (Solidus), °C 1380
1620
Specific Heat Capacity, J/kg-K 480
540
Thermal Expansion, µm/m-K 13
8.7

Otherwise Unclassified Properties

Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 4.8
47
Embodied Energy, MJ/kg 68
800
Embodied Water, L/kg 180
470

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
64
Resilience: Unit (Modulus of Resilience), kJ/m3 270
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
24
Thermal Shock Resistance, points 18
26

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
0
Hydrogen (H), % 0
0 to 0.0080
Iron (Fe), % 51.9 to 62.1
0 to 0.12
Manganese (Mn), % 4.0 to 6.0
0
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 11.5 to 13.5
0
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0 to 0.015
Oxygen (O), % 0
0.080 to 0.16
Palladium (Pd), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
99.417 to 99.8
Vanadium (V), % 0.1 to 0.3
0