EN 1.3956 Stainless Steel vs. Solder Alloy 116

EN 1.3956 stainless steel belongs to the iron alloys classification, while solder alloy 116 belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.3956 stainless steel and the bottom bar is solder alloy 116.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
26
Elongation at Break, % 27
18
Poisson's Ratio 0.28
0.42
Shear Modulus, GPa 79
9.3
Tensile Strength: Ultimate (UTS), MPa 650
34

Thermal Properties

Latent Heat of Fusion, J/g 300
34
Melting Completion (Liquidus), °C 1420
260
Melting Onset (Solidus), °C 1380
180
Specific Heat Capacity, J/kg-K 480
160
Thermal Expansion, µm/m-K 13
27

Otherwise Unclassified Properties

Base Metal Price, % relative 22
90
Density, g/cm3 7.8
10
Embodied Carbon, kg CO2/kg material 4.8
7.2
Embodied Energy, MJ/kg 68
120
Embodied Water, L/kg 180
690

Common Calculations

Stiffness to Weight: Axial, points 14
1.5
Stiffness to Weight: Bending, points 25
9.8
Strength to Weight: Axial, points 23
0.94
Strength to Weight: Bending, points 21
2.3
Thermal Shock Resistance, points 18
3.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 51.9 to 62.1
0 to 0.020
Lead (Pb), % 0
68.4 to 70.5
Manganese (Mn), % 4.0 to 6.0
0
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 11.5 to 13.5
0 to 0.010
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
29.5 to 30.5
Vanadium (V), % 0.1 to 0.3
0
Zinc (Zn), % 0
0 to 0.0010