EN 1.3961 alloy belongs to the iron alloys classification, while AWS BAg-19 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.3961 alloy and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
74
Poisson's Ratio 0.3
0.37
Shear Modulus, GPa 72
27
Tensile Strength: Ultimate (UTS), MPa 450
140

Thermal Properties

Latent Heat of Fusion, J/g 270
120
Melting Completion (Liquidus), °C 1430
890
Melting Onset (Solidus), °C 1390
760
Specific Heat Capacity, J/kg-K 460
250
Thermal Expansion, µm/m-K 1.3
20

Otherwise Unclassified Properties

Density, g/cm3 8.2
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.0
Stiffness to Weight: Bending, points 23
14
Strength to Weight: Axial, points 15
3.8
Strength to Weight: Bending, points 16
5.8
Thermal Shock Resistance, points 130
6.9

Alloy Composition

Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 0 to 0.25
0
Copper (Cu), % 0
6.6 to 7.9
Iron (Fe), % 60.7 to 65
0
Lithium (Li), % 0
0.15 to 0.3
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 35 to 37
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
92 to 93
Sulfur (S), % 0 to 0.020
0
Residuals, % 0
0 to 0.15