EN 1.3961 Alloy vs. EN 1.8519 Steel

Both EN 1.3961 alloy and EN 1.8519 steel are iron alloys. Both are furnished in the quenched and tempered condition. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3961 alloy and the bottom bar is EN 1.8519 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 31
10
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 300
710
Tensile Strength: Ultimate (UTS), MPa 450
1200
Tensile Strength: Yield (Proof), MPa 310
1030

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 1.3
13

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.1
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.9
Embodied Energy, MJ/kg 66
26
Embodied Water, L/kg 110
58

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 250
2790
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 15
43
Strength to Weight: Bending, points 16
32
Thermal Shock Resistance, points 130
35

Alloy Composition

Carbon (C), % 0 to 0.050
0.27 to 0.34
Chromium (Cr), % 0 to 0.25
2.3 to 2.7
Iron (Fe), % 60.7 to 65
95.7 to 97.1
Manganese (Mn), % 0 to 0.5
0.4 to 0.7
Molybdenum (Mo), % 0 to 1.0
0.15 to 0.25
Nickel (Ni), % 35 to 37
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.035
Vanadium (V), % 0
0.1 to 0.2