EN 1.3961 Alloy vs. C19010 Copper
EN 1.3961 alloy belongs to the iron alloys classification, while C19010 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.3961 alloy and the bottom bar is C19010 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 31 | |
| 2.4 to 22 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Shear Strength, MPa | 300 | |
| 210 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 450 | |
| 330 to 640 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 260 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1060 |
| Melting Onset (Solidus), °C | 1390 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Expansion, µm/m-K | 1.3 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 31 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 66 | |
| 42 |
| Embodied Water, L/kg | 110 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 7.3 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 290 to 1680 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 15 | |
| 10 to 20 |
| Strength to Weight: Bending, points | 16 | |
| 12 to 18 |
| Thermal Shock Resistance, points | 130 | |
| 12 to 23 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 0 | |
| 97.3 to 99.04 |
| Iron (Fe), % | 60.7 to 65 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 35 to 37 | |
| 0.8 to 1.8 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.010 to 0.050 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |