EN 1.3961 Alloy vs. N06025 Nickel
EN 1.3961 alloy belongs to the iron alloys classification, while N06025 nickel belongs to the nickel alloys. They have 46% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.3961 alloy and the bottom bar is N06025 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 31 | |
| 32 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 76 |
| Shear Strength, MPa | 300 | |
| 500 |
| Tensile Strength: Ultimate (UTS), MPa | 450 | |
| 760 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1350 |
| Melting Onset (Solidus), °C | 1390 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Expansion, µm/m-K | 1.3 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 50 |
| Density, g/cm3 | 8.2 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 8.4 |
| Embodied Energy, MJ/kg | 66 | |
| 120 |
| Embodied Water, L/kg | 110 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 240 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 15 | |
| 26 |
| Strength to Weight: Bending, points | 16 | |
| 22 |
| Thermal Shock Resistance, points | 130 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 1.8 to 2.4 |
| Carbon (C), % | 0 to 0.050 | |
| 0.15 to 0.25 |
| Chromium (Cr), % | 0 to 0.25 | |
| 24 to 26 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 60.7 to 65 | |
| 8.0 to 11 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.15 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 35 to 37 | |
| 59.2 to 65.9 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.1 to 0.2 |
| Yttrium (Y), % | 0 | |
| 0.050 to 0.12 |
| Zinc (Zn), % | 0 | |
| 0.010 to 0.1 |