EN 1.3961 Alloy vs. ZK60A Magnesium
EN 1.3961 alloy belongs to the iron alloys classification, while ZK60A magnesium belongs to the magnesium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.3961 alloy and the bottom bar is ZK60A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 46 |
| Elongation at Break, % | 31 | |
| 4.5 to 9.9 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 18 |
| Shear Strength, MPa | 300 | |
| 170 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 450 | |
| 320 to 330 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Melting Completion (Liquidus), °C | 1430 | |
| 600 |
| Melting Onset (Solidus), °C | 1390 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 960 |
| Thermal Expansion, µm/m-K | 1.3 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 13 |
| Density, g/cm3 | 8.2 | |
| 1.9 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 23 |
| Embodied Energy, MJ/kg | 66 | |
| 160 |
| Embodied Water, L/kg | 110 | |
| 940 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 14 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 570 to 690 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 63 |
| Strength to Weight: Axial, points | 15 | |
| 47 to 49 |
| Strength to Weight: Bending, points | 16 | |
| 55 to 56 |
| Thermal Shock Resistance, points | 130 | |
| 19 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 60.7 to 65 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 92.5 to 94.8 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 35 to 37 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 4.8 to 6.2 |
| Zirconium (Zr), % | 0 | |
| 0.45 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |