EN 1.3963 Alloy vs. EN 1.7362 Steel
Both EN 1.3963 alloy and EN 1.7362 steel are iron alloys. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.3963 alloy and the bottom bar is EN 1.7362 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 29 | |
21 to 22 |
Poisson's Ratio | 0.3 | |
0.29 |
Shear Modulus, GPa | 72 | |
74 |
Shear Strength, MPa | 290 | |
320 to 370 |
Tensile Strength: Ultimate (UTS), MPa | 440 | |
510 to 600 |
Tensile Strength: Yield (Proof), MPa | 310 | |
200 to 360 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
260 |
Melting Completion (Liquidus), °C | 1430 | |
1460 |
Melting Onset (Solidus), °C | 1390 | |
1420 |
Specific Heat Capacity, J/kg-K | 460 | |
470 |
Thermal Expansion, µm/m-K | 1.6 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 25 | |
4.5 |
Density, g/cm3 | 8.2 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 4.8 | |
1.8 |
Embodied Energy, MJ/kg | 66 | |
23 |
Embodied Water, L/kg | 110 | |
69 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
90 to 110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
100 to 340 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 23 | |
25 |
Strength to Weight: Axial, points | 15 | |
18 to 21 |
Strength to Weight: Bending, points | 16 | |
18 to 20 |
Thermal Shock Resistance, points | 110 | |
14 to 17 |
Alloy Composition
Carbon (C), % | 0 to 0.050 | |
0.1 to 0.15 |
Chromium (Cr), % | 0 to 0.25 | |
4.0 to 6.0 |
Copper (Cu), % | 0 | |
0 to 0.3 |
Iron (Fe), % | 60.5 to 64.9 | |
91.5 to 95.2 |
Manganese (Mn), % | 0 to 0.5 | |
0.3 to 0.6 |
Molybdenum (Mo), % | 0 to 1.0 | |
0.45 to 0.65 |
Nickel (Ni), % | 35 to 37 | |
0 to 0.3 |
Nitrogen (N), % | 0 | |
0 to 0.012 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.020 |
Silicon (Si), % | 0 to 0.5 | |
0 to 0.5 |
Sulfur (S), % | 0.1 to 0.2 | |
0 to 0.0050 |