EN 1.3963 Alloy vs. S44626 Stainless Steel
Both EN 1.3963 alloy and S44626 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.3963 alloy and the bottom bar is S44626 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 29 | |
| 23 |
| Poisson's Ratio | 0.3 | |
| 0.27 |
| Shear Modulus, GPa | 72 | |
| 80 |
| Shear Strength, MPa | 290 | |
| 340 |
| Tensile Strength: Ultimate (UTS), MPa | 440 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1440 |
| Melting Onset (Solidus), °C | 1390 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Expansion, µm/m-K | 1.6 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 14 |
| Density, g/cm3 | 8.2 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 2.9 |
| Embodied Energy, MJ/kg | 66 | |
| 42 |
| Embodied Water, L/kg | 110 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 300 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 23 | |
| 26 |
| Strength to Weight: Axial, points | 15 | |
| 19 |
| Strength to Weight: Bending, points | 16 | |
| 19 |
| Thermal Shock Resistance, points | 110 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 to 0.25 | |
| 25 to 27 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 60.5 to 64.9 | |
| 68.1 to 74.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.75 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0.75 to 1.5 |
| Nickel (Ni), % | 35 to 37 | |
| 0 to 0.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.75 |
| Sulfur (S), % | 0.1 to 0.2 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0.2 to 1.0 |