EN 1.3967 Stainless Steel vs. EN 1.4405 Stainless Steel

Both EN 1.3967 stainless steel and EN 1.4405 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.3967 stainless steel and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 22
17
Fatigue Strength, MPa 240
370
Impact Strength: V-Notched Charpy, J 74
68
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 690
860
Tensile Strength: Yield (Proof), MPa 350
610

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1070
870
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 16
11

Otherwise Unclassified Properties

Base Metal Price, % relative 25
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
2.8
Embodied Energy, MJ/kg 66
39
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 36
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
130
Resilience: Unit (Modulus of Resilience), kJ/m3 310
950
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
31
Strength to Weight: Bending, points 22
26
Thermal Shock Resistance, points 15
29

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 20 to 21.5
15 to 17
Iron (Fe), % 50.3 to 57.8
73.6 to 80.3
Manganese (Mn), % 4.0 to 6.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0.7 to 1.5
Nickel (Ni), % 15 to 17
4.0 to 6.0
Niobium (Nb), % 0 to 0.25
0
Nitrogen (N), % 0.2 to 0.35
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.010
0 to 0.025