EN 1.3967 Stainless Steel vs. EN 1.8965 Steel

Both EN 1.3967 stainless steel and EN 1.8965 steel are iron alloys. They have 57% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3967 stainless steel and the bottom bar is EN 1.8965 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 22
16
Fatigue Strength, MPa 240
220
Impact Strength: V-Notched Charpy, J 74
30
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 690
570
Tensile Strength: Yield (Proof), MPa 350
340

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1070
420
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.8
Embodied Energy, MJ/kg 66
25
Embodied Water, L/kg 180
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
78
Resilience: Unit (Modulus of Resilience), kJ/m3 310
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
20
Strength to Weight: Bending, points 22
19
Thermal Shock Resistance, points 15
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0 to 0.030
0 to 0.19
Chromium (Cr), % 20 to 21.5
0.35 to 0.85
Copper (Cu), % 0
0.2 to 0.6
Iron (Fe), % 50.3 to 57.8
94.6 to 99
Manganese (Mn), % 4.0 to 6.0
0.45 to 1.6
Molybdenum (Mo), % 3.0 to 3.5
0 to 0.35
Nickel (Ni), % 15 to 17
0 to 0.7
Niobium (Nb), % 0 to 0.25
0 to 0.065
Nitrogen (N), % 0.2 to 0.35
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.010
0 to 0.035
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14
Zirconium (Zr), % 0
0 to 0.17