EN 1.3967 Stainless Steel vs. SAE-AISI 50B60 Steel

Both EN 1.3967 stainless steel and SAE-AISI 50B60 steel are iron alloys. They have 56% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3967 stainless steel and the bottom bar is SAE-AISI 50B60 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
180 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 22
12 to 20
Fatigue Strength, MPa 240
240 to 330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 690
610 to 630
Tensile Strength: Yield (Proof), MPa 350
350 to 530

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1070
410
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.4
Embodied Energy, MJ/kg 66
19
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
71 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 310
330 to 750
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
22 to 23
Strength to Weight: Bending, points 22
20 to 21
Thermal Shock Resistance, points 15
20

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0 to 0.030
0.56 to 0.64
Chromium (Cr), % 20 to 21.5
0.4 to 0.6
Iron (Fe), % 50.3 to 57.8
97.3 to 98.1
Manganese (Mn), % 4.0 to 6.0
0.75 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 15 to 17
0
Niobium (Nb), % 0 to 0.25
0
Nitrogen (N), % 0.2 to 0.35
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040