EN 1.4002 Stainless Steel vs. EN 1.7706 Steel

Both EN 1.4002 stainless steel and EN 1.7706 steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4002 stainless steel and the bottom bar is EN 1.7706 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
17
Fatigue Strength, MPa 160
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 500
690
Tensile Strength: Yield (Proof), MPa 260
500

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 760
440
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
3.7
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
2.3
Embodied Energy, MJ/kg 27
32
Embodied Water, L/kg 100
57

Common Calculations

PREN (Pitting Resistance) 13
4.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
670
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 8.1
11
Thermal Shock Resistance, points 18
20

Alloy Composition

Aluminum (Al), % 0.1 to 0.3
0
Carbon (C), % 0 to 0.080
0.15 to 0.2
Chromium (Cr), % 12 to 14
1.2 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 83.6 to 87.9
94.7 to 97.1
Manganese (Mn), % 0 to 1.0
0.5 to 0.9
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.015
Vanadium (V), % 0
0.2 to 0.3