EN 1.4005 Stainless Steel vs. C19010 Copper
EN 1.4005 stainless steel belongs to the iron alloys classification, while C19010 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4005 stainless steel and the bottom bar is C19010 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 13 to 21 | |
| 2.4 to 22 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 43 |
| Shear Strength, MPa | 390 to 450 | |
| 210 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 750 | |
| 330 to 640 |
| Tensile Strength: Yield (Proof), MPa | 370 to 500 | |
| 260 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 200 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1060 |
| Melting Onset (Solidus), °C | 1400 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 260 |
| Thermal Expansion, µm/m-K | 10 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 48 to 63 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 48 to 63 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 31 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 28 | |
| 42 |
| Embodied Water, L/kg | 100 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 110 | |
| 7.3 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 to 650 | |
| 290 to 1680 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 10 to 20 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 75 |
| Thermal Shock Resistance, points | 23 to 27 | |
| 12 to 23 |
Alloy Composition
| Carbon (C), % | 0.060 to 0.15 | |
| 0 |
| Chromium (Cr), % | 12 to 14 | |
| 0 |
| Copper (Cu), % | 0 | |
| 97.3 to 99.04 |
| Iron (Fe), % | 82.4 to 87.8 | |
| 0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.010 to 0.050 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |