EN 1.4006 Stainless Steel vs. QE22A Magnesium
EN 1.4006 stainless steel belongs to the iron alloys classification, while QE22A magnesium belongs to the magnesium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.4006 stainless steel and the bottom bar is QE22A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 44 |
| Elongation at Break, % | 16 to 23 | |
| 2.4 |
| Fatigue Strength, MPa | 150 to 300 | |
| 110 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 17 |
| Shear Strength, MPa | 370 to 460 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 750 | |
| 250 |
| Tensile Strength: Yield (Proof), MPa | 230 to 510 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 250 |
| Melting Completion (Liquidus), °C | 1440 | |
| 640 |
| Melting Onset (Solidus), °C | 1400 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 970 |
| Thermal Conductivity, W/m-K | 30 | |
| 110 |
| Thermal Expansion, µm/m-K | 11 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 120 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 2.0 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 27 |
| Embodied Energy, MJ/kg | 27 | |
| 220 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 to 110 | |
| 5.5 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 660 | |
| 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 60 |
| Strength to Weight: Axial, points | 21 to 27 | |
| 36 |
| Strength to Weight: Bending, points | 20 to 24 | |
| 46 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 59 |
| Thermal Shock Resistance, points | 21 to 26 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 83.1 to 88.4 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 93.1 to 95.8 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.75 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 2.0 to 3.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Unspecified Rare Earths, % | 0 | |
| 1.8 to 2.5 |
| Zirconium (Zr), % | 0 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |