EN 1.4006 Stainless Steel vs. C42200 Brass
EN 1.4006 stainless steel belongs to the iron alloys classification, while C42200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4006 stainless steel and the bottom bar is C42200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 16 to 23 | |
| 2.0 to 46 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 76 | |
| 42 |
| Shear Strength, MPa | 370 to 460 | |
| 210 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 750 | |
| 300 to 610 |
| Tensile Strength: Yield (Proof), MPa | 230 to 510 | |
| 100 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 170 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1040 |
| Melting Onset (Solidus), °C | 1400 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Conductivity, W/m-K | 30 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 31 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 32 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 29 |
| Density, g/cm3 | 7.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 2.7 |
| Embodied Energy, MJ/kg | 27 | |
| 44 |
| Embodied Water, L/kg | 100 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 to 110 | |
| 12 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 660 | |
| 49 to 1460 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 27 | |
| 9.5 to 19 |
| Strength to Weight: Bending, points | 20 to 24 | |
| 11 to 18 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 39 |
| Thermal Shock Resistance, points | 21 to 26 | |
| 10 to 21 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 86 to 89 |
| Iron (Fe), % | 83.1 to 88.4 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.75 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.35 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.8 to 1.4 |
| Zinc (Zn), % | 0 | |
| 8.7 to 13.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |