EN 1.4016 Stainless Steel vs. EN 1.4417 Stainless Steel

Both EN 1.4016 stainless steel and EN 1.4417 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4016 stainless steel and the bottom bar is EN 1.4417 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 22
25
Fatigue Strength, MPa 190
380
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
81
Tensile Strength: Ultimate (UTS), MPa 520
730
Tensile Strength: Yield (Proof), MPa 290
550

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 870
1100
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
17
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
21
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.1
4.1
Embodied Energy, MJ/kg 29
57
Embodied Water, L/kg 120
180

Common Calculations

PREN (Pitting Resistance) 17
41
Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
170
Resilience: Unit (Modulus of Resilience), kJ/m3 210
730
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 6.7
4.6
Thermal Shock Resistance, points 19
20

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 16 to 18
24 to 26
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 79.9 to 84
56.7 to 66.9
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
6.0 to 8.5
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.020
Tungsten (W), % 0
0 to 1.0