EN 1.4020 Stainless Steel vs. AISI 440A Stainless Steel
Both EN 1.4020 stainless steel and AISI 440A stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4020 stainless steel and the bottom bar is AISI 440A stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 13 to 34 | |
| 5.0 to 20 |
| Fatigue Strength, MPa | 340 to 540 | |
| 270 to 790 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Shear Strength, MPa | 510 to 680 | |
| 450 to 1040 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1130 | |
| 730 to 1790 |
| Tensile Strength: Yield (Proof), MPa | 430 to 950 | |
| 420 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 760 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1480 |
| Melting Onset (Solidus), °C | 1350 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.0 |
| Density, g/cm3 | 7.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 2.2 |
| Embodied Energy, MJ/kg | 37 | |
| 31 |
| Embodied Water, L/kg | 150 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 23 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 220 | |
| 87 to 120 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 28 to 41 | |
| 26 to 65 |
| Strength to Weight: Bending, points | 25 to 32 | |
| 23 to 43 |
| Thermal Shock Resistance, points | 16 to 23 | |
| 26 to 65 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 16.5 to 19 | |
| 16 to 18 |
| Iron (Fe), % | 62.8 to 71.8 | |
| 78.4 to 83.4 |
| Manganese (Mn), % | 11 to 14 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0.2 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |