EN 1.4020 Stainless Steel vs. EN 1.0434 Steel
Both EN 1.4020 stainless steel and EN 1.0434 steel are iron alloys. They have 68% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4020 stainless steel and the bottom bar is EN 1.0434 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 340 | |
| 110 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 13 to 34 | |
| 12 to 28 |
| Fatigue Strength, MPa | 340 to 540 | |
| 190 to 300 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 510 to 680 | |
| 280 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1130 | |
| 390 to 540 |
| Tensile Strength: Yield (Proof), MPa | 430 to 950 | |
| 250 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 400 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1460 |
| Melting Onset (Solidus), °C | 1350 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 1.8 |
| Density, g/cm3 | 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 37 | |
| 18 |
| Embodied Water, L/kg | 150 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 220 | |
| 39 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 2290 | |
| 170 to 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 41 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 25 to 32 | |
| 15 to 19 |
| Thermal Shock Resistance, points | 16 to 23 | |
| 12 to 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.15 | |
| 0.15 to 0.19 |
| Chromium (Cr), % | 16.5 to 19 | |
| 0 |
| Iron (Fe), % | 62.8 to 71.8 | |
| 98.8 to 99.18 |
| Manganese (Mn), % | 11 to 14 | |
| 0.65 to 0.85 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0.2 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |