EN 1.4020 Stainless Steel vs. ZA-8
EN 1.4020 stainless steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.4020 stainless steel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 340 | |
| 87 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 85 to 86 |
| Elongation at Break, % | 13 to 34 | |
| 1.3 to 8.0 |
| Fatigue Strength, MPa | 340 to 540 | |
| 51 to 100 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 77 | |
| 34 |
| Shear Strength, MPa | 510 to 680 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1130 | |
| 210 to 370 |
| Tensile Strength: Yield (Proof), MPa | 430 to 950 | |
| 210 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 100 |
| Melting Completion (Liquidus), °C | 1390 | |
| 400 |
| Melting Onset (Solidus), °C | 1350 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Expansion, µm/m-K | 17 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 11 |
| Density, g/cm3 | 7.6 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 3.3 |
| Embodied Energy, MJ/kg | 37 | |
| 62 |
| Embodied Water, L/kg | 150 | |
| 420 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 220 | |
| 2.8 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 2290 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 28 to 41 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 25 to 32 | |
| 12 to 18 |
| Thermal Shock Resistance, points | 16 to 23 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.0 to 8.8 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 16.5 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.8 to 1.3 |
| Iron (Fe), % | 62.8 to 71.8 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 11 to 14 | |
| 0 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 0 to 0.020 |
| Nitrogen (N), % | 0.2 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.045 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 89.7 to 91.2 |