EN 1.4021 Stainless Steel vs. EN 1.0580 Steel
Both EN 1.4021 stainless steel and EN 1.0580 steel are iron alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4021 stainless steel and the bottom bar is EN 1.0580 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 5.6 to 25 |
| Fatigue Strength, MPa | 240 to 380 | |
| 210 to 270 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 390 to 530 | |
| 340 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 880 | |
| 540 to 620 |
| Tensile Strength: Yield (Proof), MPa | 390 to 670 | |
| 290 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 400 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 30 | |
| 51 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 27 | |
| 18 |
| Embodied Water, L/kg | 100 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 88 to 110 | |
| 31 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 1160 | |
| 230 to 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 31 | |
| 19 to 22 |
| Strength to Weight: Bending, points | 21 to 26 | |
| 19 to 21 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 14 |
| Thermal Shock Resistance, points | 22 to 31 | |
| 17 to 20 |
Alloy Composition
| Carbon (C), % | 0.16 to 0.25 | |
| 0 to 0.22 |
| Chromium (Cr), % | 12 to 14 | |
| 0 |
| Iron (Fe), % | 83.2 to 87.8 | |
| 97.5 to 100 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.6 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.55 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.045 |