EN 1.4024 Stainless Steel vs. ACI-ASTM CD4MCuN Steel

Both EN 1.4024 stainless steel and ACI-ASTM CD4MCuN steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4024 stainless steel and the bottom bar is ACI-ASTM CD4MCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 22
18
Fatigue Strength, MPa 220 to 300
340
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 590 to 750
770
Tensile Strength: Yield (Proof), MPa 330 to 510
550

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 760
1100
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
17
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
18
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
3.5
Embodied Energy, MJ/kg 27
49
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 13
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 660
760
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 27
28
Strength to Weight: Bending, points 20 to 24
24
Thermal Diffusivity, mm2/s 8.1
4.5
Thermal Shock Resistance, points 21 to 26
21

Alloy Composition

Carbon (C), % 0.12 to 0.17
0 to 0.040
Chromium (Cr), % 12 to 14
24.5 to 26.5
Copper (Cu), % 0
2.7 to 3.3
Iron (Fe), % 83.8 to 87.9
59.5 to 66.3
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
1.7 to 2.3
Nickel (Ni), % 0
4.7 to 6.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.040