EN 1.4024 Stainless Steel vs. AISI 304 Stainless Steel
Both EN 1.4024 stainless steel and AISI 304 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.4024 stainless steel and the bottom bar is AISI 304 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 15 to 22 | |
| 8.0 to 43 |
| Fatigue Strength, MPa | 220 to 300 | |
| 210 to 440 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 77 |
| Shear Strength, MPa | 370 to 460 | |
| 400 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 750 | |
| 580 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 330 to 510 | |
| 230 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 710 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1450 |
| Melting Onset (Solidus), °C | 1400 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 16 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 15 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 3.0 |
| Embodied Energy, MJ/kg | 27 | |
| 43 |
| Embodied Water, L/kg | 100 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 110 | |
| 86 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 660 | |
| 140 to 1870 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 27 | |
| 21 to 42 |
| Strength to Weight: Bending, points | 20 to 24 | |
| 20 to 32 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 4.2 |
| Thermal Shock Resistance, points | 21 to 26 | |
| 12 to 25 |
Alloy Composition
| Carbon (C), % | 0.12 to 0.17 | |
| 0 to 0.080 |
| Chromium (Cr), % | 12 to 14 | |
| 18 to 20 |
| Iron (Fe), % | 83.8 to 87.9 | |
| 66.5 to 74 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |