EN 1.4029 Stainless Steel vs. ACI-ASTM CF10SMnN Steel
Both EN 1.4029 stainless steel and ACI-ASTM CF10SMnN steel are iron alloys. They have 76% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4029 stainless steel and the bottom bar is ACI-ASTM CF10SMnN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 10 to 20 | |
| 34 |
| Fatigue Strength, MPa | 270 to 400 | |
| 260 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 930 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 410 to 740 | |
| 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 340 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 900 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1360 |
| Melting Onset (Solidus), °C | 1400 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 500 |
| Thermal Expansion, µm/m-K | 10 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 15 |
| Density, g/cm3 | 7.7 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 3.1 |
| Embodied Energy, MJ/kg | 28 | |
| 45 |
| Embodied Water, L/kg | 100 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 120 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 to 1410 | |
| 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 25 to 33 | |
| 24 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 22 |
| Thermal Shock Resistance, points | 26 to 34 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.25 to 0.32 | |
| 0 to 0.1 |
| Chromium (Cr), % | 12 to 13.5 | |
| 16 to 18 |
| Iron (Fe), % | 82.8 to 87.6 | |
| 59.1 to 65.4 |
| Manganese (Mn), % | 0 to 1.5 | |
| 7.0 to 9.0 |
| Molybdenum (Mo), % | 0 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 9.0 |
| Nitrogen (N), % | 0 | |
| 0.080 to 0.18 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 1.0 | |
| 3.5 to 4.5 |
| Sulfur (S), % | 0.15 to 0.25 | |
| 0 to 0.030 |