EN 1.4029 Stainless Steel vs. EN 1.4162 Stainless Steel

Both EN 1.4029 stainless steel and EN 1.4162 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4029 stainless steel and the bottom bar is EN 1.4162 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 10 to 20
32
Fatigue Strength, MPa 270 to 400
410
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 440 to 550
520
Tensile Strength: Ultimate (UTS), MPa 700 to 930
780
Tensile Strength: Yield (Proof), MPa 410 to 740
520

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
430
Maximum Temperature: Mechanical, °C 750
1000
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
15
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
12
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.6
Embodied Energy, MJ/kg 28
38
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 14
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 89 to 120
220
Resilience: Unit (Modulus of Resilience), kJ/m3 440 to 1410
690
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25 to 33
28
Strength to Weight: Bending, points 23 to 27
25
Thermal Diffusivity, mm2/s 8.1
4.0
Thermal Shock Resistance, points 26 to 34
21

Alloy Composition

Carbon (C), % 0.25 to 0.32
0 to 0.040
Chromium (Cr), % 12 to 13.5
21 to 22
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 82.8 to 87.6
67.2 to 73.3
Manganese (Mn), % 0 to 1.5
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.6
0.1 to 0.8
Nickel (Ni), % 0
1.4 to 1.9
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0.15 to 0.25
0 to 0.015