EN 1.4029 Stainless Steel vs. SAE-AISI 1037 Steel

Both EN 1.4029 stainless steel and SAE-AISI 1037 steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4029 stainless steel and the bottom bar is SAE-AISI 1037 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 10 to 20
14 to 20
Fatigue Strength, MPa 270 to 400
220 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 440 to 550
360 to 390
Tensile Strength: Ultimate (UTS), MPa 700 to 930
580 to 640
Tensile Strength: Yield (Proof), MPa 410 to 740
320 to 540

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
1.4
Embodied Energy, MJ/kg 28
18
Embodied Water, L/kg 100
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 89 to 120
83 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 440 to 1410
270 to 780
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 33
20 to 23
Strength to Weight: Bending, points 23 to 27
20 to 21
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 26 to 34
18 to 20

Alloy Composition

Carbon (C), % 0.25 to 0.32
0.32 to 0.38
Chromium (Cr), % 12 to 13.5
0
Iron (Fe), % 82.8 to 87.6
98.5 to 99
Manganese (Mn), % 0 to 1.5
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.6
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0.15 to 0.25
0 to 0.050