EN 1.4034 Stainless Steel vs. Grade N12MV Nickel
EN 1.4034 stainless steel belongs to the iron alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4034 stainless steel and the bottom bar is grade N12MV nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 11 to 14 | |
| 6.8 |
| Fatigue Strength, MPa | 230 to 400 | |
| 130 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 76 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 900 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 390 to 730 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 770 | |
| 900 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1620 |
| Melting Onset (Solidus), °C | 1390 | |
| 1570 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 11 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 75 |
| Density, g/cm3 | 7.7 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 16 |
| Embodied Energy, MJ/kg | 27 | |
| 200 |
| Embodied Water, L/kg | 100 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 to 94 | |
| 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 1370 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 25 to 32 | |
| 18 |
| Strength to Weight: Bending, points | 22 to 27 | |
| 17 |
| Thermal Shock Resistance, points | 24 to 32 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.43 to 0.5 | |
| 0 to 0.12 |
| Chromium (Cr), % | 12.5 to 14.5 | |
| 0 to 1.0 |
| Iron (Fe), % | 83 to 87.1 | |
| 4.0 to 6.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 0 | |
| 60.2 to 69.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.6 |