EN 1.4062 Stainless Steel vs. EN 1.3538 Steel
Both EN 1.4062 stainless steel and EN 1.3538 steel are iron alloys. They have 76% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is EN 1.3538 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 800 | |
| 670 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1030 | |
| 440 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1380 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 41 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 3.0 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.6 |
| Embodied Energy, MJ/kg | 37 | |
| 21 |
| Embodied Water, L/kg | 150 | |
| 56 |
Common Calculations
| PREN (Pitting Resistance) | 27 | |
| 3.3 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 24 to 26 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 22 to 23 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 11 |
| Thermal Shock Resistance, points | 21 to 22 | |
| 20 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.030 | |
| 0.93 to 1.1 |
| Chromium (Cr), % | 21.5 to 24 | |
| 1.7 to 2.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 69.3 to 77.3 | |
| 96 to 97.2 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 0 to 0.45 | |
| 0.4 to 0.5 |
| Nickel (Ni), % | 1.0 to 2.9 | |
| 0 |
| Nitrogen (N), % | 0.16 to 0.28 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |