EN 1.4062 Stainless Steel vs. EN 1.6580 Steel

Both EN 1.4062 stainless steel and EN 1.6580 steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is EN 1.6580 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23 to 34
11 to 19
Fatigue Strength, MPa 410 to 420
310 to 610
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 510
450 to 700
Tensile Strength: Ultimate (UTS), MPa 770 to 800
720 to 1170
Tensile Strength: Yield (Proof), MPa 530 to 600
460 to 990

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1030
450
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
4.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.8
Embodied Energy, MJ/kg 37
23
Embodied Water, L/kg 150
59

Common Calculations

PREN (Pitting Resistance) 27
3.3
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
560 to 2590
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28 to 29
26 to 41
Strength to Weight: Bending, points 24 to 25
23 to 31
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 21 to 22
21 to 34

Alloy Composition

Carbon (C), % 0 to 0.030
0.26 to 0.34
Chromium (Cr), % 21.5 to 24
1.8 to 2.2
Iron (Fe), % 69.3 to 77.3
93.7 to 95.5
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.45
0.3 to 0.5
Nickel (Ni), % 1.0 to 2.9
1.8 to 2.2
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035