EN 1.4062 Stainless Steel vs. EN 1.6582 Steel

Both EN 1.4062 stainless steel and EN 1.6582 steel are iron alloys. They have 77% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is EN 1.6582 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770 to 800
620 to 1750

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1030
440
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
3.6
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.7
Embodied Energy, MJ/kg 37
22
Embodied Water, L/kg 150
56

Common Calculations

PREN (Pitting Resistance) 27
2.2
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28 to 29
22 to 62
Strength to Weight: Bending, points 24 to 25
21 to 41
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 21 to 22
18 to 51

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.38
Chromium (Cr), % 21.5 to 24
1.3 to 1.7
Iron (Fe), % 69.3 to 77.3
94.7 to 96.5
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.45
0.15 to 0.3
Nickel (Ni), % 1.0 to 2.9
1.3 to 1.7
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035