MakeItFrom.com
Menu (ESC)

EN 1.4062 Stainless Steel vs. Z21721 Zinc

EN 1.4062 stainless steel belongs to the iron alloys classification, while Z21721 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is Z21721 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 23 to 34
40
Poisson's Ratio 0.27
0.25
Shear Modulus, GPa 79
35
Tensile Strength: Ultimate (UTS), MPa 770 to 800
150
Tensile Strength: Yield (Proof), MPa 530 to 600
120

Thermal Properties

Latent Heat of Fusion, J/g 290
110
Maximum Temperature: Mechanical, °C 1030
90
Melting Completion (Liquidus), °C 1430
410
Melting Onset (Solidus), °C 1380
390
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
37

Otherwise Unclassified Properties

Base Metal Price, % relative 12
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 2.6
2.8
Embodied Energy, MJ/kg 37
53
Embodied Water, L/kg 150
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
57
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
88
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 28 to 29
6.4
Strength to Weight: Bending, points 24 to 25
9.6
Thermal Diffusivity, mm2/s 4.0
44
Thermal Shock Resistance, points 21 to 22
4.8

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.070
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0
Copper (Cu), % 0
0 to 0.0050
Iron (Fe), % 69.3 to 77.3
0 to 0.010
Lead (Pb), % 0
0 to 1.0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
0
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
98.9 to 100