EN 1.4104 Stainless Steel vs. AWS ER120S-1
Both EN 1.4104 stainless steel and AWS ER120S-1 are iron alloys. They have 83% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4104 stainless steel and the bottom bar is AWS ER120S-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 23 | |
| 17 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 750 | |
| 930 |
| Tensile Strength: Yield (Proof), MPa | 350 to 560 | |
| 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 260 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1390 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 25 | |
| 46 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.5 | |
| 4.2 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 1.9 |
| Embodied Energy, MJ/kg | 30 | |
| 25 |
| Embodied Water, L/kg | 120 | |
| 56 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 77 to 120 | |
| 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 800 | |
| 1850 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 33 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 27 |
| Thermal Diffusivity, mm2/s | 6.7 | |
| 13 |
| Thermal Shock Resistance, points | 22 to 27 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0.1 to 0.17 | |
| 0 to 0.1 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 0 to 0.6 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 78.8 to 84.1 | |
| 92.4 to 96.1 |
| Manganese (Mn), % | 0 to 1.5 | |
| 1.4 to 1.8 |
| Molybdenum (Mo), % | 0.2 to 0.6 | |
| 0.3 to 0.65 |
| Nickel (Ni), % | 0 | |
| 2.0 to 2.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.25 to 0.6 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |